牌號
|
X7CrNiAl 17-7不銹彈簧鋼絲
|
|
|
|
|
|
|
|
|
德國W-Nr.
|
1.4568
|
|
|
|
|
|
|
|
|
對應標準
|
DIN EN 10270-3-2012
|
|
|
|
|
|
|
|
|
機械彈簧鋼絲—第3部分：不銹彈簧鋼絲
|
|
|
|
|
|
|
|
|
Steel wire for mechanical springs – Part 3: Stainless spring steel wire
|
|
|
|
|
|
|
|
|
歸類
|
沉淀硬化型不銹鋼
|
|
|
|
|
|
|
|
|
性能
|
彈性 耐腐蝕
|
|
|
|
|
|
|
|
|
X7CrNiAl17-7 化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni *
|
Al
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
16
|
6.5
|
0.7
|
|
最DA值
|
0.09
|
0.7
|
1
|
0.04
|
0.015
|
18
|
7.8
|
1.5
|
|
*為提高冷成形性能，可將鎳含量上限提高至8.30%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
X7CrNiAl17-7 機械性能
|
|
|
|
|
|
|
|
|
|
直徑
|
抗拉強度
|
|
|
|
|
|
|
|
|
d
|
σb
|
|
|
|
|
|
|
|
|
mm
|
ksi
|
|
|
|
|
|
|
|
|
d ≤ 0.2
|
1975~2280
|
|
|
|
|
|
|
|
|
0.2 <d≤ 0.3
|
1950~2250
|
|
|
|
|
|
|
|
|
0.3<d≤ 0.4
|
1925~2220
|
|
|
|
|
|
|
|
|
0.4<d≤ 0.5
|
1900~2190
|
|
|
|
|
|
|
|
|
0.5<d≤ 0.65
|
1850~2130
|
|
|
|
|
|
|
|
|
0.65<d≤ 0.8
|
1825~2100
|
|
|
|
|
|
|
|
|
0.8<d≤ 1
|
1800~2070
|
|
|
|
|
|
|
|
|
1<d≤ 1.25
|
1750~2020
|
|
|
|
|
|
|
|
|
1.25<d≤ 1.5
|
1700~1960
|
|
|
|
|
|
|
|
|
1.5<d≤ 1.75
|
1650~1900
|
|
|
|
|
|
|
|
|
1.75<d≤ 2
|
1600~1840
|
|
|
|
|
|
|
|
|
2<d≤ 2.5
|
1550~1790
|
|
|
|
|
|
|
|
|
2.5<d≤ 3
|
1500~1730
|
|
|
|
|
|
|
|
|
3<d≤ 3.5
|
1450~1670
|
|
|
|
|
|
|
|
|
3.5<d≤ 4.25
|
1400~1610
|
|
|
|
|
|
|
|
|
4.25<d≤ 5
|
1350~1560
|
|
|
|
|
|
|
|
|
5<d≤ 6
|
1300~1500
|
|
|
|
|
|
|
|
|
6<d≤ 7
|
1250~1440
|
|
|
|
|
|
|
|
|
7<d≤ 8.5
|
1250~1440
|
|
|
|
|
|
|
|
|
8.5<d≤ 10
|
1240~1440
|
|
|
|
|
|
|
|
|
對于本牌號鋼絲制造的彈簧，其特性不僅取決于拉絲本身的特性，還取決于彈簧的熱處理(見A.2)。因此本牌號鋼在拉伸后通過熱處理來滿足機械性能。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|