不銹鋼材質和標準對應表 TP316L不銹鋼管
|
0Cr17Ni12Mo2化學成分質量分數/%?--GB/T14976-2002
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni?
|
Cr
|
Mo
|
|
≤0.08%
|
≤1.00%
|
≤2.0%
|
≤0.035%
|
≤0.03%
|
10.0%-14.0%
|
16.0%-18.5%
|
2.00-3.00
|
|
00Cr17Ni14Mo2化學成分質量分數/%?--GB/T14976-2002
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni?
|
Cr
|
Mo
|
|
≤0.03%
|
≤1.00%
|
≤2.0%
|
≤0.035%
|
≤0.03%
|
12.0%-15.0%
|
16.0%-18%
|
2.00-3.00
|
|
06Cr17Ni12Mo2化學成分質量分數/%? GB/T14976-2012
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni?
|
Cr
|
Mo
|
|
≤0.08%
|
≤1.00%
|
≤2.0%
|
≤0.045%
|
≤0.03%
|
10.0%-14.0%
|
16.0%-18%
|
2.00-3.00
|
|
022Cr17Ni12Mo2化學成分質量分數/%? GB/T14976-2012
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni?
|
Cr
|
Mo
|
|
≤0.03%
|
≤1.00%
|
≤2.0%
|
≤0.045%
|
≤0.03%
|
10.0%-14.0%
|
16.0%-18.5%
|
2.00-3.00
|
|
TP316化學成分質量分數/%?--ASTM?A312
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni?
|
Cr
|
Mo
|
|
≤0.08%
|
≤1.00%
|
≤2.0%
|
≤0.045%
|
≤0.03%
|
11.0%-14.0%
|
16.0%-18%
|
2.00-3.00
|
|
TP316L化學成分質量分數/%?--ASTM?A312
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni?
|
Cr
|
Mo
|
|
≤0.035%
|
≤1.00%
|
≤2.0%
|
≤0.045%
|
≤0.03%
|
10.0%-14.0%
|
16.0%-18%
|
2.00-3.00
|
?
補充說明：
一?
????
|
? ? ? ? ? 舊牌號??
|
新牌號
|
備注
|
|
? ? ?0Cr17Ni12Mo2? ? ? ? ? ? ? ??
|
06Cr17Ni12Mo2? ? ? ? ?
|
一一對應關系
|
|
? ? ?00Cr17Ni14Mo2
|
022Cr17Ni12Mo2
|
一一對應關系
|
二?在不銹鋼管行業，0Cr17Ni12Mo2，06Cr17Ni12Mo2，022Cr17Ni12Mo2三個價格一致，00Cr17Ni14Mo2因為鎳含量高2%，所有價格高出約4500元/噸。
三?建議采用材質和標準的一一對應關系。例：0Cr17Ni12Mo2和00Cr17Ni14Mo2對應GB/T14976-2002。TP316和TP316L都對應ASTM?A312標準。
06Cr17Ni12Mo2和00Cr17Ni14Mo2無對應執行標準，只有牌號標準。
四?以上如有混淆，建議采用0Cr17Ni12Mo2材質，對應標準GB/T14976-2002
五?以上如有錯誤，請以國家標準為準。