OK 74.46是一款含有0.5% Mo合金化成分的LMA焊條，可用于焊接壓力容器鋼種。使用特性非常適合傾斜位置的接頭焊接。其藥皮成分經過針對低電流焊接的優化，因而OK 74.46非常適合用于管道的焊接。
Typical Tensile Properties
|
PWHT 620°C 1h
|
|
Elongation
|
Tensile Strength
|
Yield Strength
|
保護氣體
|
|
27 %
|
560 MPa
|
460 MPa
|
ISO
|
|
-
|
-
|
-
|
AWS
|
夏比V型缺口沖擊性能
|
PWHT 620°C 1h
|
|
Impact Value
|
Testing Temperature
|
保護氣體
|
|
175 J
|
20 °C
|
ISO
|
焊縫金屬分析
|
Mn
|
|
Mn
|
Mo
|
C
|
Si
|
Cr
|
|
0.77 %
|
-
|
-
|
-
|
-
|
|
Mo
|
|
Mn
|
Mo
|
C
|
Si
|
Cr
|
|
-
|
0.57 %
|
-
|
-
|
-
|
|
C
|
|
Mn
|
Mo
|
C
|
Si
|
Cr
|
|
-
|
-
|
0.05 %
|
-
|
-
|
|
Si
|
|
Mn
|
Mo
|
C
|
Si
|
Cr
|
|
-
|
-
|
-
|
0.38 %
|
-
|
|
Cr
|
|
Mn
|
Mo
|
C
|
Si
|
Cr
|
|
-
|
-
|
-
|
-
|
0.04 %
|
熔敷數據
|
Fusion time per electrode at 90% I max
|
kg weld metal/kg electrodes
|
Number of electrodes/kg weld metal
|
安培
|
熔敷率
|
電壓 V
|
直徑
|
|
40 sec
|
0.59 kg
|
136.0
|
55-80 A
|
0.7 kg/h
|
22 V
|
2.0 x 300 mm
|
|
55 sec
|
0.59 kg
|
73.0
|
75-110 A
|
0.9 kg/h
|
23 V
|
2.5 x 350 mm
|
|
66 sec
|
0.54 kg
|
53
|
105-150 A
|
1 kg/h
|
23 V
|
3.2 x 350 mm
|
|
81 sec
|
0.59 kg
|
37.0
|
105-150 A
|
1.2 kg/h
|
25 V
|
3.2 x 450 mm
|
|
90 sec
|
0.65 kg
|
22.5
|
140-200 A
|
1.8 kg/h
|
26 V
|
4.0 x 450 mm
|
|
104 sec
|
0.65 kg
|
14.5
|
190-270 A
|
2.4 kg/h
|
27 V
|
5.0 x 450 mm
|