| 產品參數 | | 品牌 | KEYFLEX | | 產品特性 | 28DTPEE | | 是否進口 | 否 | | 產地 | 韓國 | | 廠家(產地) | LG化學 | | 牌號 | BT1028D | | 銷售方式 | 品牌經銷 | | 品名 | TPEE | | 加工級別 | 注塑級 | | 特性級別 | 標準級、***、耐老化 | | 用途級別 | 汽車部件 | | 可售賣地 | 全國 | | 類型 | 標準料 | | 韓國LG TPEE KEYFLEX BT 1028D注塑級 Density / Specific Gravity | 1.05 | g/cm3 | ASTM D792 | Melt Mass-Flow Rate (MFR)?(230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 | Molding Shrinkage - Flow?(3.20 mm) | 0.40 to 0.80 | | ASTM D955 | Water Absorption?(24 hr, 23°C) | 0.80 | | ASTM D570 | | Hardness | Nominal Value | Unit | Test Method | Durometer Hardness |
|
| ASTM D2240 | Shore A | 75 |
|
| Shore D | 25 |
|
|
| Mechanical | Nominal Value | Unit | Test Method | Tensile Strength?3?(Break, 2.00 mm) | 19.6 | MPa | ASTM D638 | Tensile Elongation?3?(Break, 2.00 mm) | 900 | | ASTM D638 | | Impact | Nominal Value | Unit | Test Method | Notched Izod Impact |
|
| ASTM D256 | -40°C, 6.40 mm | No Break |
|
| 23°C, 6.40 mm | No Break |
|
|
| Thermal | Nominal Value | Unit | Test Method | Peak Melting Temperature | 155 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method | Comparative Tracking Index?(Solution A) | 600 | V | IEC 60112 | | Flammability | Nominal Value | Unit | Test Method | Flame Rating |
|
| UL 94 | 1.5 mm | HB |
|
| 3.0 mm | HB |
|
|
TPEE具有 的耐熱性能，硬度越高，耐熱性越好；TPEE在110～140℃連續加熱10h基本不失重，在160℃和180℃分別加熱10h，失重僅為0.05和0.1，因而TPEE的使用溫度非常高，短期使用溫度更高，能適應汽車生產線上的烘漆溫度(150～160℃)，并且它在高低溫下機械性能損失小。TPEE在120℃以上使用，其拉伸強度遠遠高于TPU此外TPEE還具有 耐低溫性能，TPEE脆點低于-70℃并且硬度越低，耐寒性越好，大部分TPEE可在-40℃下長期使用。由于TPEE在高、低溫時表現出的均衡性能，它的工作溫度范圍非常寬，可在-70～200℃使用。 .jpg)
|