| 產品參數 | | 品牌 | Delrin | | 產品特性 | 高***POM | | 是否進口 | 否 | | 產地 | 美國 | | 廠家(產地) | 美國杜邦 | | 牌號 | 500cl | | 銷售方式 | 品牌經銷 | | 品名 | POM | | 加工級別 | 注塑級 | | 特性級別 | *** | | 產品規格 | 25KG/包 | | 可售賣地 | 全國 | | 類型 | 標準料 | | 高 POM Delrin 500CL
?POM強度、剛度高，彈性好，減磨 性好。其力學性能 ，比強度可達50.5MPa，比剛度可達2650MPa，與金屬十分接近。POM的力學性能隨溫度變化小，共聚POM比均聚POM的變化稍大一點。POM的沖擊強度較高，但常規沖擊不及ABS和PC；POM對缺口敏感，有缺口可使沖擊強度下降90之多。
? Density | 1.41 | g/cm3 | ISO 1183 | Melt Mass-Flow Rate (MFR)?(190°C/2.16 kg) | 15 | g/10 min | ISO 1133 | Melt Volume-Flow Rate (MVR)?(190°C/2.16 kg) | 12 | cm3/10min | ISO 1133 | Molding Shrinkage |
|
| ISO 294-4 | Across Flow | 1.8 | |
| Flow | 1.9 | |
| Water Absorption |
|
| ISO 62 | Saturation, 23°C, 2.00 mm | 1.0 | |
| Equilibrium, 23°C, 2.00 mm, 50 RH | 0.25 | |
| | Hardness | Nominal Value | Unit | Test Method | Rockwell Hardness |
|
| ISO 2039-2 | M-Scale | 92 |
|
| R-Scale | 120 |
|
|
| Mechanical | Nominal Value | Unit | Test Method | Tensile Modulus | 3100 | MPa | ISO 527-1 | Tensile Stress?(Yield) | 70.0 | MPa | ISO 527-2 | Tensile Strain?(Yield) | 15 | | ISO 527-2 | Nominal Tensile Strain at Break | 25 | | ISO 527-2 | Flexural Modulus | 2900 | MPa | ISO 178 | Poisson&＃39;s Ratio | 0.37 |
|
| | Impact | Nominal Value | Unit | Test Method | Charpy Notched Impact Strength |
|
| ISO 179/1eA | -30°C | 7.0 | kJ/m2 |
| 23°C | 8.0 | kJ/m2 |
| Charpy Unnotched Impact Strength |
|
| ISO 179/1eU | -30°C | 290 | kJ/m2 |
| 23°C | 350 | kJ/m2 |
| Notched Izod Impact Strength |
|
| ISO 180/1A | -40°C | 9.0 | kJ/m2 |
| 23°C | 9.0 | kJ/m2 |
|
| Thermal | Nominal Value | Unit | Test Method | Deflection Temperature Under Load |
|
|
| 0.45 MPa, Unannealed | 158 | °C | ISO 75-2/B | 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A | Vicat Softening Temperature | 160 | °C | ISO 306/B50 | Melting Temperature?2 | 178 | °C | ISO 11357-3 | CLTE |
|
| ISO 11359-2 | Flow | 1.1E-4 | cm/cm/°C |
| Transverse | 1.1E-4 | cm/cm/°C |
| Annealing Temperature | 160 | °C |
| Annealing Time - Optional | 30.0 | min/mm |
|
.jpg)
.jpg)
|
.jpg)