| 產(chǎn)品參數(shù) | | 品牌 | KOPEL | | 產(chǎn)品特性 | 高回彈TPEE | | 是否進(jìn)口 | 否 | | 產(chǎn)地 | 韓國 | | 廠家(產(chǎn)地) | 韓國科隆 | | 牌號(hào) | KP3335HR | | 銷售方式 | 品牌經(jīng)銷 | | 品名 | TPEE | | 加工級(jí)別 | 注塑級(jí)、擠出級(jí) | | 特性級(jí)別 | 抗紫外線、***、耐老化、耐候 | | 可售賣地 | 全國 | | 類型 | 標(biāo)準(zhǔn)料 | | 科隆高回彈TPEE KOPEL KP3335HR Density / Specific Gravity | 1.18 | g/cm3 | ASTM D792 | Melt Mass-Flow Rate (MFR)?(220°C/2.16 kg) | 14 | g/10 min | ASTM D1238 | Molding Shrinkage - Flow | 1.2 | | ASTM D955 | Water Absorption?(24 hr, 23°C) | 0.50 | | ASTM D570 | | Hardness | Nominal Value | Unit | Test Method | Durometer Hardness?(Shore D) | 55 |
| ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method | Tensile Strength?2?(Break, 3.20 mm) | 18.0 | MPa | ASTM D638 | Tensile Elongation?2?(Break, 3.20 mm) | 560 | | ASTM D638 | Flexural Modulus?2?(3.20 mm) | 165 | MPa | ASTM D790 | Flexural Strength?2?(3.20 mm) | 10.0 | MPa | ASTM D790 | | Impact | Nominal Value | Unit | Test Method | Notched Izod Impact |
|
| ASTM D256 | -30°C, 6.40 mm | No Break |
|
| 23°C, 6.40 mm | No Break |
|
|
| Thermal | Nominal Value | Unit | Test Method | Vicat Softening Temperature | 169 | °C | ASTM D1525?3 | Peak Melting Temperature?4 | 195 | °C | ASTM D3418 |
| Flammability | Nominal Value |
| Test Method | Flame Rating?(0.8 mm) | HB |
| UL 94 |
TPEE具有 的耐油性，在室溫下能耐大多數(shù)極性液體化學(xué)介質(zhì)(如酸、堿、胺二醇類化合物)，但對(duì)鹵代烴(氟里昂除外)及酚類的作用卻無能為力，其耐化學(xué)品的能力隨其硬度的提高而提高。TPEE對(duì)大多數(shù)有機(jī)溶劑、燃料及氣體的抗溶脹性能和抗?jié)B透性能是好的，對(duì)燃油滲透性僅為氯丁膠、氯磺化聚乙烯、丁腈膠等耐油橡膠的1/3～1/300但TPEE耐熱水性較差，添加聚碳酰亞胺穩(wěn)定劑可以明顯改善其抗水解性能。 .jpg)
|