性能項目
|
測試條件
|
測試方法
|
數值/描述
|
單位
|
|
機械性能
|
拉伸強度(引張強度)
|
|
ASTM D638/ISO 527
|
9.8
|
kg/cm2(MPa)[Lb/in2]
|
|
|
斷裂伸長率
|
|
ASTM D638/ISO 527
|
600
|
%
|
|
|
拉伸模量
|
|
ASTM D638/ISO 527
|
|
kg/cm2(MPa)[Lb/in2]
|
|
|
拉伸屈服伸長率(延伸率)
|
|
ASTM D638/ISO 527
|
|
%
|
|
|
拉伸斷裂伸長率(延伸率)
|
|
ASTM D638/ISO 527
|
|
%
|
|
|
彎曲模量(彎曲彈性率)
|
|
ASTM D790/ISO 178
|
|
kg/cm2(MPa)[Lb/in2]
|
|
|
彎曲強度
|
|
ASTM D790/ISO 178
|
|
kg/cm2(MPa)[Lb/in2]
|
|
|
洛氏硬度
|
|
ASTM D785
|
|
|
|
|
IZOD 缺口沖擊強度
|
1/4" 23℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
|
|
1/4" -30℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
|
|
1/8" 23℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
|
|
1/8" -30℃
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
|
Charpy沖擊強度
|
23℃ （缺口）
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
|
|
-30℃（缺口）
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
|
|
23℃（無缺口）
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
|
|
-30℃（無缺口）
|
ASTM D256/ISO 179
|
|
kg·cm/cm(J/M)ft·lb/in
|
|
物性性能
|
比重（密度）
|
|
ASTM D792/ISO 1183
|
0.917
|
|
|
|
成型收縮率
|
|
ASTM D955
|
|
%
|
|
|
熔融指數（流動系數）
|
200℃/5kg
|
ASTM D1238/ISO 1133
|
35
|
g/10min
|
|
|
|
220℃/10kg
|
ASTM D1238/ISO 1133
|
|
g/10min
|
|
|
吸水率 23℃/24H
|
|
ASTM D570/ISO 62
|
|
%
|
|
熱性能
|
熱變形溫度
|
退火
|
ASTM D648/ISO 75
|
|
℃（℉）
|
|
|
|
未退火
|
ASTM D648/ISO 75
|
|
℃（℉）
|
|
|
維卡軟化點
|
|
ASTM D1525/ISO R306
|
|
℃（℉）
|
|
|
熔點
|
|
-
|
105
|
℃（℉）
|
|
|
燃燒性（率）
|
|
UL94
|
|
|
|
|
線性膨脹系數
|
|
ASTM D696/ISO 11359
|
|
mm/mm.℃
|
|
加工條件
|
干燥條件
|
|
|
|
|
|
|
加工溫度
|
射嘴
|
|
|
℃
|
|
|
|
料筒前段
|
|
|
℃
|
|
|
|
料筒中段
|
|
|
℃
|
|
|
|
料筒后段
|
|
|
℃
|
|
|
熔體溫度
|
|
|
|
℃
|
|
|
模具溫度
|
|
|
|
℃
|
|
|
壓力
|
注塑壓力
|
|
|
Mpa
|
|
|
|
保壓壓力
|
|
|
Mpa
|
|
|
|
背壓
|
|
|
Mpa
|
|
|
螺桿轉速
|
|
|
|
rpm
|
|
其他
|
備注
|
|
|