耐高溫尼龍 防火阻燃PA6 泰國宇部 1013NW8 標準級 工程塑膠原料
發布者：t461025037 發布時間：2016-01-14 13:13:15
|
性能項目
|
試驗條件[狀態]
|
測試方法
|
測試數據
|
數據單位
|
|
基本性能
|
吸水率
|
|
ASTM D-570
|
10.7
|
%
|
|
成型收縮率
|
|
UBEmethod
|
1.3
|
%
|
|
吸水率
|
|
ASTM D-570
|
1.8
|
%
|
|
成型收縮率
|
|
UBEmethod
|
1.2
|
%
|
|
物理性能
|
比重
|
|
ASTM D-792
|
1.14
|
|
|
機械性能
|
硬度（洛氏、布氏）
|
23°
|
ASTM D-785
|
120
|
|
|
彎曲強度
|
-30°
|
ASTM D-790
|
1400
|
kgf/cm2
|
|
擠剪強度
|
23°
|
ASTM D-732
|
650
|
kgf/cm2
|
|
1%變形下的壓縮強度
|
23°
|
ASTM D-695
|
100
|
kgf/cm2
|
|
擠剪強度
|
23°
|
ASTM D-732
|
600
|
kgf/cm2
|
|
彎曲強度
|
23°
|
ASTM D-790
|
400
|
kgf/cm2
|
|
TABER磨耗率
|
|
ASTM D-1044
|
7
|
mg
|
|
抗沖擊強度
|
23°
|
ASTM D-256
|
50
|
kgf.cm/cm
|
|
斷裂下的伸張強度
|
23°
|
ASTM D-638
|
650
|
kgf/cm2
|
|
彎曲強度
|
-30°
|
ASTM D-790
|
1300
|
kgf/cm2
|
|
彎曲強度
|
80°
|
ASTM D-790
|
260
|
kgf/cm2
|
|
屈服下的伸張強度
|
-30°
|
ASTM D-638
|
1100
|
kgf/cm2
|
|
屈服下的延伸率
|
23°
|
ASTM D-638
|
8
|
%
|
|
彎曲彈性率
|
80°
|
ASTM D-256
|
4000
|
kgf.cm/cm
|
|
屈服下的伸張強度
|
23°
|
ASTM D-638
|
420
|
kgf/cm2
|
|
硬度（洛氏、布氏）
|
23°
|
ASTM D-785
|
85
|
|
|
1%變形下的壓縮強度
|
23°
|
ASTM D-695
|
200
|
kgf/cm2
|
|
屈服下的伸張強度
|
-30°
|
ASTM D-638
|
900
|
kgf/cm2
|
|
屈服下的伸張強度
|
80°
|
ASTM D-638
|
200
|
kgf/cm2
|
|
硬度（洛氏、布氏）
|
23°
|
ASTM D-785
|
55
|
|
|
抗沖擊強度
|
-30°
|
ASTM D-256
|
4.5
|
kgf.cm/cm
|
|
斷裂下的延伸率
|
23°
|
ASTM D-638
|
100
|
%
|
|
屈服下的伸張強度
|
23°
|
ASTM D-638
|
800
|
kgf/cm2
|
|
斷裂下的延伸率
|
23°
|
ASTM D-638
|
>200
|
%
|
|
彎曲彈性率
|
-30°
|
ASTM D-790
|
29000
|
kgf/cm2
|
|
彎曲彈性率
|
23°
|
ASTM D-790
|
28500
|
kgf/cm2
|
|
彎曲強度
|
23°
|
ASTM D-790
|
1100
|
kgf/cm2
|
|
抗沖擊強度
|
23°
|
ASTM D-256
|
6.5
|
kgf.cm/cm
|
|
彎曲強度
|
80°
|
ASTM D-790
|
500
|
kgf/cm2
|
|
屈服下的伸張強度
|
80°
|
ASTM D-638
|
320
|
kgf/cm2
|
|
彎曲彈性率
|
-30°
|
ASTM D-790
|
30000
|
kgf/cm2
|
|
彎曲彈性率
|
23°
|
ASTM D-790
|
7700
|
kgf/cm2
|
|
彎曲彈性率
|
80°
|
ASTM D-790
|
7500
|
kgf/cm2
|
|
硬度（洛氏、布氏）
|
23°
|
ASTM D-785
|
85
|
|
|
電氣性能
|
介電常數
|
103HZ
|
ASTM D-150
|
8.0
|
|
|
介電損耗
|
106HZ
|
ASTM D-150
|
0.02
|
|
|
體積電阻率
|
|
ASTM D-257
|
1012
|
Ω.cm
|
|
介電常數
|
60HZ
|
ASTM D-150
|
9.0
|
|
|
IEC電路
|
|
UL746
|
600+
|
V
|
|
介電常數
|
60HZ
|
ASTM D-150
|
3.9
|
|
|
介電常數
|
106HZ
|
ASTM D-150
|
3.5
|
|
|
介電損耗
|
103HZ
|
ASTM D-150
|
0.10
|
|
|
抗電弧強度
|
|
ASTM D-495
|
119
|
S
|
|
介電常數
|
103HZ
|
ASTM D-150
|
3.8
|
|
|
介電損耗
|
103HZ
|
ASTM D-150
|
0.02
|
|
|
絕緣耐力
|
|
ASTM D-149
|
20
|
KV/mm
|
|
介電損耗
|
60HZ
|
ASTM D-150
|
0.10
|
|
|
介電損耗
|
106HZ
|
ASTM D-150
|
0.12
|
|
|
介電常數
|
106HZ
|
ASTM D-150
|
4.5
|
|
|
介電損耗
|
60HZ
|
ASTM D-150
|
0.01
|
|
|
體積電阻率
|
|
ASTM D-257
|
1015
|
Ω.cm
|
|
熱性能
|
熱變形溫度
|
18.6kgf/cm2
|
ASTM D-648
|
75
|
°C
|
|
熔點
|
DSC
|
|
215-225
|
°C
|
|
線性熱膨脹系數
|
|
ASTM D-696
|
8
|
X的10-5cm/cm/°C
|
|
熱變形溫度
|
4.6kgf/cm2
|
ASTM D-648
|
180
|
°C
|
|
燃燒率
|
|
UL94
|
V-2
|