HB-YD114(Q) |
1.6 |
50-55 (受強烈后 After high impact) |
高錳鋼堆焊焊絲，受強烈后，表面具有加工硬度的特點。 High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening. |
|
HB-YD115(Q) |
1.6 |
50-55 (受強烈后After high impact) |
用于受嚴重高錳鋼堆焊，加工硬化效果顯著。 Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening. |
|
HB-YD165(Q) |
1.6 |
60-65 |
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊 High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding. |
|
HB-YD172(Q) |
1.6 |
≥40 |
用于堆焊齒輪、挖泥斗、礦山機械等磨損件 Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery. |
|
HB-YD207(Q) |
1.6 |
≥50 |
用于堆焊推土機刀片，螺旋槳等磨損零件 Applied to repair surface of high wear parts, such as bulldozer blade and propeller. |
|
HB-YD212(Q) |
1.2/1.6 |
≥50 |
用于堆焊各種受磨損的機件表面，如齒輪、挖斗、礦山機械 Applied to repair surface of wear parts, such as gear mud bucket and mining machinery. |
|
HB-YD256(Q) |
1.6 |
HB≥170 |
高錳鋼堆焊，適用于破碎機等受磨損部位的堆焊 High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher. |
|
HB-YD258(Q) |
1.6 |
55-60 |
用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD265(Q) |
1.6 |
60-65 |
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊 High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding. |
|
HB-YD322(Q) |
1.6 |
≥55 |
用于堆焊各種沖模及切削刃具，兼用于修復要求耐磨損性能較高之機械零件 Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery. |
|
HB-YD327A(Q) |
1.6 |
≥55 |
專門用于模具堆焊，耐磨性能高于D322 Used tomouldsurfacing, wear resistance is better than D322. |
|
HB-YD337(Q) |
1.6 |
≥48 |
用于鑄鋼或鍛鋼上堆焊鍛模 Applied to repairforging dieatcast steelorforging steel. |
|
HB-YD397(Q) |
1.6 |
≥40 |
用于堆焊鑄鋼或鍛鋼做坯體的熱鍛�；蚨押父邚姸饶湍ゼ� Applied to repair hotforging dieatcast steelor forging steel, or highstrengthwear surfacing. |
|
HB-YD405A(Q) |
1.6 |
50-59 |
用于熱軋輥開坯輥堆焊 Applied to repair hot-rolling blooming rollor. |
|
HB-YD430A(Q) |
1.6 |
20-35 |
打底層堆焊焊絲 A backing hardfacing flux-cored Wires |
|
HB-YD488A(Q) |
1.6 |
45-50 |
用于軋輥堆焊 Applied to repair rollor |
|
HB-YD507Mo(Q) |
1.6 |
35-45 |
用于510℃以下中高壓閥門堆焊 Applied to valve which operating tdivperature is less than 510℃. |
|
HB-YD518(Q) |
1.6 |
40-50 |
用于連鑄輥堆焊 Applied to repaircontinuous caster roller |
|
HB-YD688(Q) |
1.6 |
50-60 |
用于磨煤輥打底焊(韌性好，可以多層堆焊) Used to coal roller backing welding. |
|
HB-YD788(Q) |
1.6 |
55-62 |
硬度高，可以多層堆焊。 High hardness andmulti-layer welding |
|
HB-YD888(Q) |
1.2, 1.6 |
60-65 |
硬度高，堆焊層厚度不超過6mm。 High hardness, but thethicknessofsurfacing layeris less than 6mm. |
|
HB-YD888Ni(Q) |
1.2 |
58-65 |
高鉻合金焊絲，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD988(Q) |
1.6 |
55-63 |
高鉻合金焊絲，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD990(Q) |
1.6 |
55-65 |
用于高溫耐磨堆焊。 Applied to repair surface ofhigh tdivperaturewear parts. |
|
HB-YD58(Q) |
1.6 |
55-60 |
高溫耐磨焊絲，用于化推焦機磨靴的堆焊。 high tdivperaturewear hardfacing wires, |
|
HB-YD67(Q) |
1.6 |
58-63 |
用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-YD95(Q) |
1.6 |
55-63 |
高鉻合金焊絲，用于耐磨表面堆焊 Applied to repair surface of wear parts. |
|
HB-DG7(Q) |
1.6 |
52-60 |
地鐵盾構施工刀具刃口堆焊專用，也可用于煤碳石裝載機料斗和刃口堆焊修復。 Applied to repair surface of high impact wear parts, such as shiled machine, excavator bucket and hopper of mining machinery products |