Brutus AAA全能型特種鋼焊條
Shield Metal Arc Welding(SMAW - Stick)手工焊條電弧焊
For dissimilar and all categories of steel-tool, high alloy, nickel alloy, stainless, manganese and cast steels. 適用于工具鋼、高合金鋼、鎳合金鋼、不銹鋼、錳鋼和鑄鋼等所有類別鋼間的焊接或異種焊接。
Features 功能
Strength 127,000psi/876MPa
抗拉強度高達127,000psi/876MPa
35% Elongation
35%伸長率
Excellent AC stability
卓越的交流穩定下
All positions
全位置焊接
Easy Strike and Restrike
輕松起弧和復弧
No Spatter / Easy Slag Release
無飛濺/易脫渣
Exceptional Smooth Bead
卓越平滑的焊道
Spray-Type Arc With Low Heat
低熱噴涂式電弧
Excellent Undercoating/buildup For Hardfacing
出色的打底層，適用于堆焊
Wear and Shock Resistant
耐磨和抗沖擊
Ideal For Dissimilar Steels
適用于異種鋼
Ductile, Crack Resistant Deposit
韌性、抗裂熔敷層
Use for Broken Stud Extraction(See Thread Repair & Bolt Removal)
可用于拆除斷裂螺栓（參見螺紋修理和螺栓拆卸）
Characteristics 特點
Brutus AAA has superior wear, shock and corrosion resistance and it can be used for joining dissimilar steels. In addition, Brutus AAA has a special flux coating that gives it superior operating characteristics, allowing the welder to produce an unusually strong, smooth weld deposit with minimum effort.
Brutus AAA具有優異的耐磨性、抗沖擊性和耐腐蝕性，可用于連接異種鋼。此外，Brutus AAA具有特殊的焊劑涂層，使其具有卓越的操作特性，使焊工能夠以最小的努力產生異常堅固、光滑的焊縫熔覆層。
Brutus AAA’s ease of application makes it especially suitable where precise weld control and appearance are important. Thin sections and delicate parts can be repaired easily. It gives excellent results on dies, tools, molds, gears and exposed food handling equipment. Its high strength and ductility make it useful in almost all repairs of similar or dissimilar steels.
Brutus AAA的易用性使其特別適用于精確的焊接控制和外觀非常重要的應用。薄的工件和脆弱的零件可以很容易地修復。它在模具、工具、鑄模、齒輪和外露的食品處理設備上都能獲得出色的效果。其高強度和延展性使其在幾乎所有類似或不同鋼的維修中都很有用。
Technical技術規格
Size and Amps AC/DC+(DCEP)
|
Inches |
3/32 |
1/8 |
5/32 |
|
(mm) |
(2.4) |
(3.2) |
(4.0) |
|
Amps |
45-85 |
65-125 |
85-155 |
Best Practices Application 應用
Clean weld area.
清潔焊接區域。
Bevel heavy sections.
對重型截面進行倒角。
Preheat high alloys and heavy sections to 400oF (240oC).
將高合金和重型型材預熱至400oF（240oC）。
Use short arc.
使用短弧。
Tilt electrode 15o in direction of travel.
將焊條沿行駛方向傾斜15o。
For rapid filleting, increase amps and drag electrode at 45o.
為了快速嵌縫，提高電流并在45o下拖動焊條。
Remove slag between passes.
清除焊道之間的熔渣。