Jupiter A鑄鐵焊條
Shield Metal Arc Welding(SMAW - Stick)
For all Cast Iron - Meehanite,ductile, mealleable, gray cast irons and steel to cast iron.
適用于所有鑄鐵-Meehanite孕育鑄鐵、球墨鑄鐵、可鍛鑄鐵、灰口鑄鐵和鋼至鑄鐵的焊接。
Features
亮點
High Strength 79,000psi/545MPa
抗拉強度高達79,000psi/545MPa
Use On All Weldable Grades Of Cast Iron
用于所有可焊接等級的鑄鐵
All positions
全位置焊接
Welds Over Dirt and Oil
可以在油污上直接焊接
Eliminates Porosity
無氣孔
Ideal For Cast Iron To Steel Joining
鑄鐵與鋼連接的理想選擇
Prevents Hard Spots
不會出現硬點
Easy To Use
易于使用
Machineable deposits
可加工熔敷層
Welds Over Slag
熔渣上的焊縫
Ductile Deposits
韌性熔敷層
No preheat required
不需要預熱
Characteristics
特點
Jupiter-A has been engineered for the maintenance welder who must weld dirty, oil-soaked castings of unknown compositions. Sound, non-porous welds are produced without special preparation. Successful results are possible even when the joint is restrained.
Jupiter-A專為必須焊接成分未知的臟、浸油鑄件的維護焊工設計。在無需特殊處理的情況下，即可產生完好、無孔的焊縫。即使接頭受到約束，也有可能取得成功。
Jupiter-A makes it possible to repair machines and equipment in place without expensive tear down, thereby avoiding costly down time.
Jupiter-A可以在不需要拆卸的情況下將機器和設備維修到位，從而避免了高成本的停機時間。
Technical技術規格
Size and Amps AC/DC+(DCEP)
|
Inches |
3/32 |
1/8 |
5/32 |
|
(mm) |
(2.4) |
(3.2) |
(4.0) |
|
Amps |
48-72 |
80-120 |
100-150 |
Best Practices Application 應用
Remove cracks using grinder or Electra去除裂縫。
Stop drill crack ends.實施止裂孔。
Use medium arc and stringer beads. 使用中等弧度和線狀焊道。
Skip weld and prevent overheating 跳焊并防止過熱
Light peening recommended. 建議進行輕敲擊。
For critical or heavy parts preheat to 500?F(260?C). 對于關鍵或重型零件，預熱至500?F（260?C）。
Cool slowly after welding. 焊后緩冷。