材質
|
用途
|
化學成分
|
力學能力
|
線徑（mm）
|
凈重(kg)
|
閥芯直徑(mm)
|
備注
|
|
ER304
|
主要用于焊接18Cr-8Ni鋼
|
C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%
|
拉伸強度Mpa 1200
|
0.08-0.45
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER304L
|
主要用于焊接17Cr-8Ni鋼
|
C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%
|
拉伸強度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER308
|
主要用于焊接19Cr-9Ni鋼
|
C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%
|
拉伸強度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER308L
|
主要用于焊接20Cr-9Ni鋼
|
C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%
|
拉伸強度Mpa 1200
|
0.8-4.5
|
5/12.5/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER309
|
主要用于焊接20Cr-13Ni鋼
|
C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%
|
拉伸強度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER309L
|
主要用于焊接20Cr-14Ni鋼
|
C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%
|
拉伸強度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER309Lsi
|
主要用于焊接20Cr-14Ni鋼
|
C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10%
|
拉伸強度Mpa1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER321
|
主要用于焊接16Cr-7Ni鋼
|
C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%Ti0.73
|
拉伸強度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER347
|
主要用于焊接16Cr-9Ni鋼
|
C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% （Ta+Nb）（10*C）-10
|
拉伸強度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300 0
|
MIG:0.8-1.6 TIG:1.0-4.5
|
|
ER347L
|
主要用于焊接17Cr-9Ni鋼
|
C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% （Ta+Nb）（10*C）-10
|
拉伸強度Mpa 1200
|
0.08-4.5
|
5/10/15/20
|
100/270/300 0
|
MIG:0.8-1.6 TIG:1.0-4.5
|